Neutron Diffraction Investigation of Low and High Cycle Fatigue Austenite Stainless Steels
Materials Science Forum(2000)
摘要
A series of samples from low carbon austenite stainless steels X6CrNiTi1810 (0.04 wt % C) with different degrees of low- and high-cycle fatigue were studied on the two-axis diffractometer in NPI (Rez) to obtain microstrain characteristics of austenite and martensite produced by plastic deformation during cycling. A stabilization effect of low frequency cycling with respect to the mean square microstrain above 30 %-fatigue is found because practically no evolution of neutron peak broadening was observed in the both phases in the measured samples. A similar stabilization effect after a certain number of cycles was before noted in literature. Processing of the experimental data from high-cycle fatigue samples has found the interesting phenomenon in a behaviour of microstrain in the austenite phase vs the fatigue degree. The remarkable bounce from about 50. 10(-6) up to 400. 10(-6) has happened after one million cycles. No evolution of microstrain was observed in the martensite phase.
更多查看译文
关键词
austenite,diffraction,fatigue,martensite,neutron,residual stress,steel,strain
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络