Thermal characterization of polyethylene glycols applied in the pharmaceutical technology using differential scanning calorimetry and hot stage microscopy

In the present study, the effect of the molecular weight and thermal treatments on commercial polyethylene glycols (PEG) samples used in the pharmaceutical processing technology, has been analyzed using DSC and HSM. The molecular weight of these polymers range from 1500 to 200000. Thermal investigations on the melting behavior of original PEG samples (as received from the manufacturer) showed only one single melting DSC endotherm effect before 373 K. This fact was associated to the presence of only one type of polymeric chain. Using standard conditions, PEG samples were solidified from the melt at 373 K, either by flash cooling (using liquid nitrogen and an ice bath) and by slow cooling, soaked and by slow cooling at room temperature. They were further studied by DSC. It was found that after cooling, PEG with molecular weight 1500 and 15000 showed DSC thermograms with a single endothermic peak. However, thermograms for PEG 4000 and 6000 produced a splitted melting endotherm. This fact was attributed to the presence of two types of chains, that are the folded and extended chains. Ageing time influences also the shape of the DSC endothermal effects. It was concluded that the endotherms obtained after heating these PEG indicate that the thermal history determine the structure (extended or folded chain type forms) and the degree of crystallinity, as evidenced by changes in heat of fusion values, melting points and structures after crystallization. The relationships between melting enthalpies and melting points, as deduced from DSC diagrams, with molecular weight of the polymers are also presented.