Constitutional and microstructural investigation of the pseudobinary NiAl–W system
Intermetallics(2011)
摘要
Pseudobinary NiAl–W section in the range 0.7–1.8 at% was characterised regarding solidification microstructure and constitution. The existence of eutectic reaction was confirmed and occurs at temperature of 1664 ± 2 °C and the composition of 1.5 at% W. As-cast microstructures indicated that the NiAl–W system is an anomalous eutectic with skewed coupled zone and that the NiAl phase is a preferential phase for eutectic nucleation. Directionally solidified alloy containing 1.5 at% W exhibited entirely eutectic structure characterised by eutectic cells with the average value of 500 μm, interfibre spacing 3.5 μm, fibre diameter 300 nm, and volume fraction of the W phase 1.4%. The solubility of W in the intermetallic phase is <0.04 at% and the solubility of Ni and Al in the W phase is negligible. Crystallographic orientation between the constituent phases was established to be cube on cube. Based on the results obtained by DTA, microstructural and compositional analysis, a new isoplethal section NiAl–W of the ternary Al–Ni–W system has been proposed.
更多查看译文
关键词
A. Nickel aluminides, based on NiAl,B. Crystallography,B. Phase diagrams,C. Crystal growth,D. Microstructure
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络