Growth of ultra-thin TiO2 films by spray pyrolysis on different substrates
Applied Surface Science(2009)
摘要
In the present study TiO2 films were deposited by spray pyrolysis method onto ITO covered glass and Si (100) substrates. The spray solution containing titanium(IV) isopropoxide, acetylacetone and ethanol was sprayed at a substrate temperature of 450°C employing 1–125 spray pulses (1s spray and 30s pause). According to AFM, continuous coverage of ITO and Si substrates with TiO2 layer is formed by 5–10 and below 5 spray pulses, respectively. XPS studies revealed that TiO2 film growth on Si substrate using up to 4 spray pulses follows 2D or layer-by-layer-growth. Above 4 spray pulses, 3D or island growth becomes dominant irrespective of the substrate. Only 50 spray pulses result in TiO2 layer with the thickness more than XPS measurement escape depth as any signal from the substrate could not be detected. TiO2 grain size remains 30nm on ITO and increases from 10–20nm to 50–100nm on Si substrate with the number of spray pulses from 1 to 125.
更多查看译文
关键词
TiO2,Spray pyrolysis,Film growth,Thin film,AFM,XPS
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络