Linear Birefringence And Dichroism Measurements For Silica Coated Iron Oxide Ferrofluids
IEEE TRANSACTIONS ON MAGNETICS(2014)
摘要
The core-shell structural SiO2/Fe3O4 nanocomposites were prepared via hydrolysis and condensation of tetraethyl orthosilicate (TEOS) by using iron oxide nanoparticles as seeds in a 2-propanol/distilled water mixed solvent using ammonia as catalyst. The water-based ferrofluid (FF) as 0.3 ml EMG 304 was adopted as the seed. The effects of ammonia aqueous amount, volume ratio of 2-propanol/distilled water, TEOS amount, and reaction time on size and dispersibilty are investigated via transmission electron microscope and X-ray diffraction. Further, the linear birefringence and dichroism measurements of silica coated FF were investigated by a Stokes polarimeter. Results indicated that the appropriate reaction parameters including volume ratio of 2-propanol/distilled water of 5: 1, ammonia solution volume of 0.5 ml, TEOS amount of 50 mg, and mechanical stirring of 1000 r/min for 3 h were found to obtain large retardance and low dichroism.
更多查看译文
关键词
Birefringence, dichroism, ferrofluid (FF), nanocomposites
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络