Structural Analysis Of Silicon Co-Implanted With Carbon And High Energy Proton For The Formation Of The Lasing G-Centre

We investigate a new approach for efficient generation of the lasing G-centre (carbon substitutional-silicon self-interstitial complex) which crucially is fully compatible with standard silicon ultra-large-scale integration technology. Silicon wafers were implanted with carbon and irradiated with high energy protons to produce self-interstitials that are crucial in the formation of the G-centre. Rutherford backscattering spectrometry (RBS) and transmission electron microscopy were used to study the structure of the post-implanted silicon samples and to investigate the behaviour of the self-interstitials and damage introduced by the carbon and proton implantation. The effect of substrate pre-amorphisation on the G-centre luminescence intensity and formation properties was also investigated by implanting Ge prior to the carbon and proton irradiation. Photoluminescence measurements and RBS results show a significantly higher G-centre peak intensity and silicon yield, respectively, in samples without pre-amorphisation. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4766390]