Wet Chemical Etching Of Molten Koh/Naoh Eutectic Alloy To Evaluate Aln Single Crystal
JOURNAL OF THE KOREAN CRYSTAL GROWTH AND CRYSTAL TECHNOLOGY(2014)
摘要
We investigated the optimal etching conditions and properties of the surface change due to molten KOH/NaOH chemical wet etching using an AlN wafer which has been put to practical use in the present study. Results were observed using a scanning electron microscope after 5 minutes etching at 350 degrees C, was found to have a surface form of the respective other Al-face, the N-face. In particular, etch-pit in the form of a hexagon, which is observed in the Al-face appeared, It was calculated at 2 x 10(6)/cm(2) similar to 10(10)/cm(2) dislocation density. In the case of N-face, lattice defects in the form of the hexagonal pyramids is formed. It was discovered that in order to observe the orientation of the wafer, which corresponds to the C-axis direction of the resulting hexagonal AlN which was analyzed using XRD (0002) and is a state of being oriented in the (0004) plane. The Radius of curvature of AlN wafer was 1.6 similar to 17 m measured by DC-XRD rocking curve position.
更多查看译文
关键词
AlN, Radius curvature, KOH/NaOH, Etching, Wet etching, Etch pit
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络