Numerical Analysis Of Cz Growth Process For Sapphire Crystal Of 300 Mm Length: Part I. Influence Of Hot Zone Structure Modification On Crystal Temperature

Czochralski (CZ) growth process is one of the most important techniques for growing high quality sapphire single crystal for LED application. In this study, the inductively-heated CZ growth processes for the sapphire crystal of 300 mm length have been analyzed numerically using finite element method. The hot zone structures were modified with the crucible geometry change and the additional insulation layer installed above the crucible. The results show that the solid-liquid interface height decreased from about 80 mm at initial stage to 40 mm after mid-stage due to achieve the growth speed balance. Also the optimal input power of the modified system was similar with the original one due to the compensation effects of the crucible geometry and additional insulation. The crystal temperature grown by the modified CZ grower was increased about 10 K than the original one. Therefore the sapphire crystal of 300 mm height was grown successfully.