Evaluation of Adhesive Bonding Quality by Acoustic Emission

Prediction of fatigue life and monitoring of fracture process for adhesively bonded CFRP composites joint have been investigated by analysis of acoustic emission signals during the fatigue and tension tests. During fatigue test, generated acoustic emission is related to stored elastic strain energy. By results of monitoring of AE event rate, fatigue process could be divided into two regions, and boundaries of two regions, fatigue cycles of the initiation of fast crack growth, were 70-80% of fatigue life even though the fatigue life were highly scattered from specimen to specimen. The result shows the possibility of predicting catastrophic failure by acoustic emission monitoring.