Electrical activation of ion implanted Si in amorphous and crystalline In 0.53 Ga 0.47 As
Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms(2014)
摘要
The effect of pre-amorphization on the electrical activation of Si implants into In0.53Ga0.47As is investigated. Electrical measurements show that Si implants into pre-amorphized and crystalline In0.53Ga0.47As yield similar levels of activation (1.0×1019cm−3 in the pre-amorphized case and 9.0×1018cm−3 in the crystalline case) upon rapid thermal annealing for 5s at 750°C despite having very different types of resulting damage in the electrically active layers. The subsequent microstructural characterization by TEM indicates that the highly defective regrown layers in the pre-amorphized substrate leads to poor mobility in the active layers, which result in lower sheet resistances. The results suggest that solid phase epitaxy (SPE) in compound semiconductors can lead to some improved activation at lower temperatures and does not prevent substitutional activation of amphoteric dopants upon post SPE annealing.
更多查看译文
关键词
Ion implantation,Semiconductors,III–V,Amorphization,Activation
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络