Influences of Si-doped graded short-period superlattice on green InGaN/GaN light-emitting diodes.

We report significant improvement in optical and electrical properties of green InGaN/GaN light-emitting diodes (LEDs) by using Sidoped graded short-period InGaN/GaN superlattice (SiGSL) formed by so called indium-conversion technique. For comparison, a conventional LED without the superlattice (C-LED) and a LED with undoped graded superlattice (unGSL-LED) were prepared, respectively. The photoluminescence (PL) intensity of the SiGSL-LED was increased more than 3 times at room temperature (RT) as compared to C-LED. The PL intensity ratios of RT to 10K for the C-LED, unGSL-LED, and SiGSL-LED were measured to be 25, 40.9, and 47.5%, respectively. The difference in carrier lifetimes between 10K and RT for the SiGSL-LED is relatively small compared to that of the C-LED, which is consistent with the variation in PL intensity. The output power of a transistor-outline type SiGSL-LED was increased more than 2 times higher than that of the C-LED. (C) 2016 Optical Society of America