Wear Rates of Larger-Diameter Cross-Linked Polyethylene at 5 to 13 Years: Does Liner Thickness or Component Position Matter?
The Journal of Arthroplasty(2017)
摘要
Background: Cross-linked polyethylene (XLPE) has demonstrated significantly reduced wear and osteolysis into the second decade for total hip arthroplasty. There is a relative paucity of data with >= 36-mm bearings. Issues include potential effects of reduced liner thickness and component position on wear, osteolysis, and mechanical failure of the bearing. Methods: Radiographs of 48 primary total hip arthroplasties with >= 36-mm modular XLPE bearings were analyzed at a minimum 5 years postoperative on serial radiographs using a validated, edge-detection-based algorithm. Subgroups were examined to assess the effect of bearing diameter, liner thickness, acetabular abduction angle, and acetabular anteversion on XLPE wear. Results: There was no significant difference in volumetric wear when subgroups were stratified by component factors: liner thickness (< 6.5 mm vs >= 6.5 mm) 40.69 mm3/y vs 24.47 mm(3)/y, respectively (P = .315); acetabular component abduction angle (< 45 degrees vs >= 45 degrees): 38.68 mm(3)/y vs 27.8 mm(3)/y, respectively (P = .522); acetabular anteversion (<20 degrees vs >= 20 degrees): 41.32 mm(3)/y vs 31.79 mm(3)/y, respectively (P = .521). There were no dislocations, mechanical failures, or revisions. There were 7 hips with volumetric wear rates >= 80 mm(3)/y; 1 had possible osteolysis. Conclusion: Larger-diameter XLPE wear was not measurably affected by liner thickness, acetabular abduction angle, or acetabular anteversion. However, there is a trend for increasing volumetric wear with increasing bearing size. Wear outliers do occur, and continued follow-up of larger-diameter XLPE bearings is warranted. (C) 2016 Elsevier Inc. All rights reserved.
更多查看译文
关键词
total hip arthroplasty,cross-linked polyethylene,wear rates,osteolysis,radiographic analysis,large-diameter bearings
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络