Preparation of Porous Nanofibers from Electrospun Polyacrylonitrile/Polyvinylidene Fluoride Composite Nanofibers by Inexpensive Salt Using for Dye Adsorption

The high surface area of porous nanofibers enhances their performance for many applications. The present study investigated electrospinning and dye adsorption properties of polymeric nanofibers which were porous by various types of salts. The salt/polyacrylonitrile/polyvinylidene fluoride composite nanofibers were electrospun, and the inexpensive salts such as sodium chloride (NaCl), sodium bicarbonate (NaHCO 3 ), or calcium chloride (CaCl 2 ) was used to manufacture the porous fibers. Subsequently, the salt was removed by a selective dissolution, and salt extraction of nanofibers was performed with the solution of hydrochloric acid (10 wt%). Salt/PVDF/PAN and porous PVDF/PAN composite nanofibers have been applied to dye adsorption of solution. The characteristics of nanofibers were studied by Fourier transform infrared microscopy (FTIR) and scanning electron microscopy (SEM) analysis. FTIR showed that the salt was extracted from PVDF/PAN nanofibers successfully, and SEM indicated that many pores were aligned with the nanofibers. The adsorption capacity of salt nanofibers webs and porous nanofibers webs for Basic Blue 41 were compared with each other, and porous fibers were obtained from NaHCO 3 having the highest dye adsorption value. Adsorption of dyes follows the Langmuir isotherm and pseudo-second order kinetics.