Dehydration Characteristics of C-S-H with Ca/Si Ratio 1.0 Prepared Via Precipitation
Journal of Wuhan University of Technology-Mater. Sci. Ed.(2018)
摘要
Calcium silicate hydrate (C-S-H) with Ca/Si ratio 1.0 was prepared via precipitation in solution and heated at various temperatures to investigate its dehydration behavior. The dehydration, structural collapse and recrystallization characteristics of C-S-H and its microstructural change during heating process were investigated by XRD, SEM, Raman and TG-DSC techniques. C-S-H gradually lost non-evaporable water upon heating, about 50% and 80% non-evaporable water was removed below 200 and 400 °C, respectively, and the rest was removed up to about 1 000 °C. At 400 °C, dehydrated C-S-H exhibited the increasing disordering of calcium/silicon environment and the decreasing symmetrical bending vibration of Si-O-Si of Q 2 silicate chains. At 650 °C non-bridging oxygen atoms (O non ) attached to silicon were almost removed, and significant structural change occurred, and at 815 °C C-S-H dehydrated to wollastonite.
更多查看译文
关键词
C-S-H,heat,dehydration,structure,morphology
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络