Dielectric spectroscopy investigation of proton transfer processes in carboxymethyl alpha-cyclodextrin polymer cross-linked by epichlorohydrin

The carboxymethyl-α-cyclodextrin polymer (cross-linked by epichlorohydrin) is investigated by dielectric spectroscopy over a frequency range of 0.1–100 kHz and the temperature ranges of 137.2–297.6 K (cooling) and 137.2–472 K (heating). Upon cooling to 288.1 K, the ac-conductivity invariance is attributed to slight changes in the topology of the H-bonded chains. From 288.1 to 244.0 K, the ac-conductivity decreases abruptly (following the Arrhenius law with Eα = 0.40 eV), whereas below 244.0 K it presents no important variations. During heating from 137.2 to 302.6 K, no thermal hysteresis is observed. From 302.6 to 364.9 K, the ac-conductivity increases (Eα = 0.71 eV), whereas above 383 K it decreases up to 436.7 K since the dehydration process has been completed and the H-bonded chains can no longer be retained. From 436.7 to 472 K, the ac-conductivity increases again (Eα = 0.76 eV) indicating the formation of “new” H-bonded chains. Curve fitting of various relaxation processes is done by Havriliak-Negami equation at selective temperatures.