Effect Of The Titanium Isopropoxide:Acetylacetone Molar Ratio On The Photocatalytic Activity Of Tio2 Thin Films

TiO2 thin films with different titanium isopropoxide (TTIP):acetylacetone (AcacH) molar ratios in solution were prepared by the chemical spray pyrolysis method. The TTIP:AcacH molar ratio in spray solution varied from 1:3 to 1:20. TiO2 films were deposited onto the glass substrates at 350 degrees C and heat-treated at 500 degrees C. The morphology, structure, surface chemical composition, and photocatalytic activity of the obtained TiO2 films were investigated. TiO2 films showed a transparency of ca 80% in the visible spectral region and a band gap of ca 3.4 eV irrespective of the TTIP:AcacH molar ratio in the spray solution. TiO2 films consist of the anatase crystalline phase with a mean crystallite size in the range of 30-40 nm. Self-cleaning properties of the films were estimated using the stearic acid (SA) test. A thin layer of 8.8-mM SA solution was spin-coated onto the TiO2 film. The degradation rate of SA as a function of irradiation time was monitored by Fourier-transform infrared spectroscopy (FTIR). An increase in the TTIP:AcacH molar ratio from 1:4 to 1:8 resulted in a ten-fold increase in the photodegradation reaction rate constant (from 0.02 to the 0.2 min(-1)) under ultraviolet light and in a four-fold increase under visible light.