Effect of rapid thermal annealing on the properties of zinc tin oxide films prepared by plasma-enhanced atomic layer deposition

The effect of rapid thermal annealing treatments on the microstructure, surface morphology, and optical characteristics of zinc tin oxide (ZTO) films produced by plasma-enhanced atomic layer deposition was investigated. The ZTO films were annealed in oxygen atmosphere for 2 min at four selected temperatures from 500 to 800 °C. The X-ray diffraction showed that the annealing temperature has a great influence on the crystalline characteristics of ZTO films. The film shows complete amorphous structure for as-deposited ZTO film. Meanwhile, the spinel zinc stannate Zn2SnO4 was obtained for the samples annealed from 500 to 800 °C, which shows polycrystalline nature. The X-ray photoelectron spectroscopy proved that the annealing process in oxygen gas can effectively can reduce the oxygen vacancy defects in the films. In addition, the photoluminescence spectroscopy manifests an ultraviolet emission with a broad peak range from 345 to 385 nm. Moreover, the ultraviolet luminescence intensity increases continuously with the increase of annealing temperature. Spectroscopic ellipsometry analyses demonstrate that the refractive index of annealed films increases as the increase of annealing temperature, while the extinction coefficient decreases gradually with the increase of annealing temperature in the visible light range.