Controlled Growth Of Cu And Cuox Thin Films From Subvalent Copper Precursors

A new Cu(I) precursor, [(COD)Cu(TFB-TFEA)] (COD = 1,5-cyclooctadiene and TFB-TFEA = N-(4,4,4-triftuorobut-1-en-3-on)-6,6,6-trifluoroethylamine) with high volatility and a clean thermal decomposition pattern was tested for thermal and plasma-assisted chemical vapor deposition (CVD). The heteroleptic configuration based on an anionic and a chelating neutral ligand unified both reactivity and sufficient stability resulting in an intrinsic molecular control over the composition of the resulting CVD deposits. The electronic influence of the ligand on the metal site was studied by 1D and 2D NMR spectroscopy, while El mass spectrometry revealed the ligand elimination cascade. Thermal and plasma CVD experiments demonstrated the suitability of the copper compound for an atom-efficient (high molecule-to-material yield) deposition of copper(0) and copper(I) oxide films that could be converted into crystalline copper(s) oxide upon heat treatment at 500 degrees C.