Thermal Analysis of Mg Hydride by Sievert's Type Automatic Apparatus

In order to apply the Sievert's type automatic apparatus to thermal analysis of hydrogen absorbing materials, the dehydrogenation of the Mg-H system was investigated. As the initial wt% of hydrogen was increased to 4.4, the peak temperature of evolution rate shifted to higher temperature. However, with the initial wt% of hydrogen higher than 4.4, peak temperature of evolution rate did not change. The peak temperatures of evolution rate obtained by automatic apparatus were almost the same as those measured by a manual apparatus. As the heating rate was increased, the peak temperatures increased; the peak temperatures for heating rates 1, 2 and 3 K/min were 664, 687 and 702 K, respectively. The activation energy for the decomposition of Mg hydride was 101 kJ/mol. The Sievert's type automatic apparatus can be successively applied to the thermal analysis of metal hydride.