The Effect of Microstructural Imperfections on Corrosion Fatigue of Additively Manufactured ER70S-6 Alloy Produced by Wire Arc Deposition

This study aims at evaluating the effect of microstructure imperfections on the corrosion fatigue performance of an ER70S-6 alloy produced by wire arc additive manufacturing (WAAM) process, in a 3.5% NaCl solution. For reference, a regular ST-37 alloy with relatively similar chemical composition was considered as a counterpart alloy. This was justified by the fact that the ER70S-6 alloy is usually used for conventional welding of ST-37 steel. The results obtained indicated that while the ST-37 alloy exhibited fatigue strength of 240 MPa in the corrosive solution, the additively manufactured ER70S-6 alloy showed fatigue strength of only 140 MPa. These differences were related to microstructural imperfections that are inherently produced during the WAAM process.