Interface Structure and Mechanical Properties of 7075Al Hybrid Composite Reinforced with Micron Ti Metal Particles Using Pressure Infiltration

Micron Ti metal particles were incorporated into SiCp / 7075Al composites using pressure infiltration. The interface structure between the Ti metal particles and the matrix during the casting processes were investigated. Results show that the dispersed unreacted Ti particles form mutual di ff usion layer at the interface without the formation of low- temperature intermetallic phases during the solidification processes. The interaction between the micron Ti and the molten aluminum alloy is subject to the mutual di ff usion coe ffi cient of Ti- Al rather than the reaction activation energy. The tensile strength and plasticity of the composite were improved simultaneously due to the high interfacial bonding strength and released thermal misfit stress cause by the incorporated Ti metal particles.