Synergy effects between Li0.42Zn0.27Ti0.11Fe2.2O4 nanoparticles and CuO-Bi2O3 mixtures in low-temperature sintered LiZnTi ferrites with enhanced gyromagnetic and microwave dielectric properties
Journal of Alloys and Compounds(2021)
摘要
Promoting grain growth and optimizing microstructure are valid strategies for enhancing gyromagnetic and microwave dielectric properties of low-temperature sintered ferrite materials. Here, a modified low-temperature sintering technique was attempted for the synthesis of LiZnTi ferrites that have compact microstructure and improved performances. Trace amounts of CuO-Bi2O3 mixtures (0.50 wt%) were adopted as sintering additives to promote grain growth and to reduce the sintering temperature. Meanwhile, Li0.42Zn0.27Ti0.11Fe2.2O4 nanoparticles (∼21.9 nm) were synthesized using a sol-gel auto-combustion method and were used to optimize the microstructure and to restrain abnormal grain growth. XRD Rietveld refinement and SEM images revealed that uniform and dense LiZnTi ferrites with single-phase spinel structure were obtained. Results demonstrated that co-doping of Li0.42Zn0.27Ti0.11Fe2.2O4 nanoparticles and CuO-Bi2O3 mixtures allows low-temperature sintering (900 °C) to be achieved and also promotes grain growth and densification. In particular, LiZnTi ferrites that were modified with 5.00 wt% Li0.42Zn0.27Ti0.11Fe2.2O4 nanoparticles and 0.50 wt% CuO-Bi2O3 sintering additives exhibited narrow ferromagnetic resonance linewidth (ΔH, ∼145 Oe) and low dielectric loss tangent (tanδε, ∼2.45 × 10−4) at ∼9.50 GHz, high saturation flux density (Bs, ∼364 mT), and high squareness ratio (Br/Bs, ∼0.89). Such a modified sintering technique at a low sintering temperature, as reported in this work, provides a reference for other advanced ferrites.
更多查看译文
关键词
LiZnTi ferrites,Li0.42Zn0.27Ti0.11Fe2.2O4 nanoparticles,CuO-Bi2O3 sintering additives,LTCC application
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络