Fabrication Of Transparent Mg(Oh)(2) Thin Films By Drop-Dry Deposition

Magnesium hydroxide (Mg(OH)(2)) thin films were deposited by the drop-dry deposition (DDD) method using an aqueous solution containing Mg(NO3)(2) and NaOH. DDD was performed by dropping the solution on a substrate, heating-drying, and rinsing in water. Effects of different deposition conditions on the surface morphology and optical properties of Mg(OH)(2) thin films were researched. Films with a thickness of 1-2 mu m were successfully deposited, and the Raman peaks of Mg(OH)(2) were observed for them. Their transmittance in the visible range was 95% or more, and the bandgap was about 5.8 eV. It was found that the thin films have resistivity of the order of 10(5) omega cm. Thus, the transparent and semiconducting Mg(OH)(2) thin films were successfully prepared by DDD.