Effects Of Elevated Temperature Treatment On Compositions And Tensile Properties Of Several Kinds Of Basalt Fibers

Five kinds of domestic basalt fibers were studied for the changes of chemical compositions, physical properties and tensile properties of these fibers before and after 200-800 degrees C treatment in air atmosphere and in nitrogen atmosphere. These works were done mainly by means of X-ray fluorescence spectrometry and fiber monofilament tensile testing methods in order to understand the elevated temperature resistance of basalt fiber. The experimental results show that the surface of basalt fibers becomes smoother with slightly smaller in diameter and mass reduction at the same time, due to the removal of fiber surface treatment agent after elevated temperature treatment in air atmosphere. Mass fractions of SiO, and Al2O, decrease while mass fractions of FeO+Fe2O3, CaO and MgO increase, among which the mass fraction of FeO+Fe2O3 increase the most with the maximum increase of 21 % The monofilament tensile strength of basalt fiber is reduced after 200 degrees C treatment and the maximum strength retention percentage is 98. 3%. The monofilament tensile strength reduces evidently after 400 degrees C treatment and the maximum strength retention percentage is 64. 6%. Moreover, the strength retention percentages of five kinds of basalt fibers are all less than 20% after 800 degrees C treatment. In addition, the fiber elongation at break decreases with the increase of treating temperature and the elastic modulus increases. Compared with that in air atmosphere, strength retention rate of basalt fiber is higher and tensile properties are more stable in nitrogen atmosphere.