Na-Influenced Bulk and Surface Properties of the So-Called Iota()-Alumina: Spectroscopy and Microscopy Studies

The test alumina (the so-called iota-Al2O3) was thermally recovered at 1,100 degrees C from chitosan-AlOx hybrid films and found to contain Na and Ca impurity ions inherited from the parent chitosan. Two different modifications of pure alumina, namely, gamma- and alpha-Al2O3, were adopted as control samples. The test and control aluminas were examined for 1) the bulk elemental constitution by atomic absorption spectroscopy (AAS), 2) the surface chemical composition by X-ray photoelectron spectroscopy (XPS), 3) the bulk phase composition by X-ray powder diffractometry (XRD), ex-situ Fourier-transform infrared spectroscopy (IR), and Laser Raman (LRa) spectroscopy, 4) the surface area, topography, and morphology by N-2 sorptiometry, and atomic force (AFM) and scanning electron microscopy (SEM), 5) the surface adsorptive interactions with pyridine and 2-propanol gas-phase molecules by in-situ IR spectroscopy of the adsorbed species, and 6) the surface catalytic interactions with 2-propanol gas-phase molecules by in-situ IR spectroscopy of the gas phase. Results obtained could clearly show that the test alumina (iota-Al2O3) is only hypothetically pure alumina since in reality its bulk structure is majored by mullite-type Na-aluminate (Na0.67Al6O9.33/NaAlO2) and minored by Na-beta-alumina (Na1.71Al11O17) and beta-alumina (NaAl11O17). Consistently, observed Na-influenced modifications of the surface chemistry, topology, and morphology, as well as adsorptive and catalytic interactions with pyridine and 2-propanol gas-phase molecules, showed significant deviations from those exhibited by the control pure aluminas (gamma- and alpha-Al2O3).