The Influence Of Wet Milling Of Aluminum And Aluminum Alloys Powder Screenings On The Characteristics Of The Aluminum-Based Pastes

The milling of aluminum powders in non-aqueous solvents is used in the production of high-quality pigment pastes of flake shapes with thickness from some microns to hundreds of nanometers. In Russia, such pigments are not produced at a large scale, however, spherical powders made from aluminum and its alloys are manufactured. Starting the production of pigments from screenings of powder production will not only solve the problem of fine fractions disposal, but also reduce the cost of the target fractions powders. The fraction of powders with an average d50 of less than similar to 20 mu m should be disposed. In this research, by varying the laboratory conditions, the parameters for milling screenings of A8 aluminum powder, AK9ch and 1201 aluminum alloys were selected. The milling was performed in non-aqueous solvents: a highly refined commercial petroleum solvent and liquid paraffin oil. The prospects of using wet milling for the manufacture of pigment pastes from alloys has been demonstrated including average thicknesses of the flakes about 40-80 nm. Thus, it has been demonstrated that wet and bead grindings lead to thinning of metal powder particles to thicknesses of less than 100 nm.