Press-On Force Effect on the Efficiency of Composite Restorations Final Polishing—Preliminary in Vitro Study

The surface texture of dental restorations has a major influence on plaque accumulation and aesthetical appearance. The study aimed to evaluate the surface roughness of composite resins depending on the varying polishing sequences and applied forces. A total of 60 samples from two composite resins (Boston and Charisma) were polymerized using a lamp with 1200 mW/cm2 intensity and covering celluloid strip. The polishing sequence consisted of 12.6 mm OptiDisc (Kerr) – with increased disc per each subsequent step. Half of the samples were polished at 1N force, with the other half at 2N. The surface roughness examination was performed using a WYKO NT930 (Veeco) optical profilometer. The selected roughness parameters were compared by ANOVA with the significance level α = 0.05. The more complex polishing sequence affected on the composite smoothness. Higher roughness was identified in Charisma samples as compared to Boston. The specimens polished with 2N force contained a slightly rougher surface than those polished with 1N. However, these differences were not statistically significant. Despite the satisfactory visual effect obtained by polishing the composite samples, the profilometric examination revealed the roughness. Finishing is crucial for providing a smooth composite surface, allowing it to function properly in the oral environment.