Positive Modification On The Mechanical, Tribological And Oxidation Properties Of Alcrnbsin Coatings By Regulating The Nb/Si-Doping Ratio

The precise control of Nb/Si-doping ratio is the critical factor to tailor AlCrNbSiN coatings with superior comprehensive properties. In this study, the effect of Nb/Si-doping ratio on the microstructure, mechanical, tribological and oxidation properties of AlCrNbSiN coatings was systematically researched. With the increase of Nb/Si-doping ratio, coatings' microstructures changed from a featureless dense structure to a columnar and equiaxed mixed microstructure gradually. The main phase was transformed from the solid solution phase of h-Al (Cr)N for Nb-free coating (Nb/Si = 0:1) to c-Al(Cr)N solid solution for three Nb-containing coatings (Nb/Si = 1:2, 1:1 and 2:1). When Nb/Si ratio is 1:1, the formation of harmful h-NbN phase was found in the coating. The performance results indicated that, (1) The AlCrNbSiN coating with the Nb/Si ratio of 2:1 achieved optimal hardness (-34.9 GPa), toughness (CPRs -569.3) and the minimum wear rate of 2.34 x 10-6 mm3/(N.m); (2) When the Nb/Si-doping ratio is 1:2, the coating exhibited the best oxidation resistance, attributing to the sufficient (Al, Si)Ox oxidation protective layer and only a small amount of AlNbO4 and CrNbO4 formed at 1200 degrees C.