Influences of Mullite Fibers on Mechanical and Thermal Properties of Silica-Based Ceramic Cores

Mullite fibers composite silica-based ceramic cores were successfully prepared by injection molding. The effects of mullite fibers on the mechanical and thermal properties of ceramic cores were investigated. The results indicated that the linear shrinkage was significantly decreased and the porosity was gradually increased with the increase of mullite fibers. In addition, the flexural strength for the room temperature and the simulated casting temperature of 1500 degrees C was increased to a maximum value when the content of mullite fibers was about 1 wt.%, and then decreased with the increase of mullite fibers. The mullite fibers of 1 wt.% presented excellent mechanical properties with a linear shrinkage of .65%, a porosity of 6.96%, and a flexural strength of 17 MPa at room temperature and 34.83 MPa at the simulated casting temperature of 1500 degrees C. Besides, the change in microstructure and properties in various contents of mullite fibers were analyzed.