Establishment of Processing Maps for 25vol.% B4CP/AA6061 Composite and Its Application in Hot Pack-Rolling Process
Materials Science Forum(2018)
摘要
The hot workability and hot pack-rolling process of B 4 C P /AA6061 composite were studied. The results showed that the addition of B 4 C particles could effectively promote the dynamic recrystallization (DRX) process of the composite. DRX and DRX grains growth were dominant deformation mechanism during hot deformation of B 4 C P /AA6061composite. Typical instability defects included micro voids and particle aggregation. The optimum processing parameters for good workability were obtained in the temperature range of 450°C-500°C and strain rate range of 0.01s -1 -0.1s -1 . According to the flow stress curves and processing maps, a temperature of 500°C and a rolling velocity of 40 mm/s were chosen for pack-rolling experiments. The pack-rolled composite sheets in the RD and TD showed more homogeneous DRX grains than as-HIPed microstructures, which might indicate that hot pack-rolling could lead to more homogeneous microstructures without any edge cracking and surface cracking.
更多查看译文
关键词
Hot Deformation,Friction Stir Processing,Processing Techniques,Metal Processing
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要