Physicochemical Properties of Dentine Subjected to Microabrasive Blasting and Its Influence on Bonding to Self-Adhesive Prosthetic Cement in Shear Bond Strength Test: an in Vitro Study

The aim of this in vitro study was to assess the influence of microabrasive blasting on the physicochemical properties of dentine and shear bond strength (SBS) of self-adhesive resin cement (Maxcem Elite, Kerr, Orange, CA, USA) bonded to the dentine surface. Ninety cylindrical specimens with exposed dentine of human teeth were prepared and divided into three randomized, parallel sample sets A, B, and C. Groups B and C were subjected to abrasive blasting using a micro-sandblasting device (Microetcher IIa, Danville Materials, Carlsbad, CA, USA) with two gradations of Al2O3 abrasives (Group B, abrasion with a gradation of 50 μm; group C, abrasion with a gradation of 27 μm). SEM imaging, profilometry, chemical composition analysis, contact angle measurements, surface free energy, and SBS tests were performed. The resulting data were statistically analyzed using the Statistica software (ver. 13.3, Tibco Software Inc., Palo Alto, CA, USA). Microabrasive blasting caused changes in surface topography, structural features, and the connection strength between the dentin surface and self-adhesive prosthetic cement. Air microabrasion through the multifactorial positive reorganization of the treated surface of dentine is recommended as a pretreatment method in fixed prosthodontics adhesive cementation protocols.