Electron transport properties in degenerate magnesium tin oxynitride (Mg1-xSn1+xN2-2yO2y) with average wurtzite structure

MgSnN2 with an average wurtzite structure (wz-MgSnN2) has recently emerged as a pseudo-III-nitride semiconductor, studied for applications in tandem solar cells, green light-emitting diodes, and other optoelectronic devices. This compound has only been researched recently, and, therefore, its charge-carrier transport properties are poorly understood. Understanding these properties is essential for optoelectronic applications. In this study, we grew wz-Mg1-xSn1+xN2 biaxially oriented polycrystalline films with x = -0.08 to 0.29 by reactive sputtering and investigated the charge-carrier transport properties using both direct current and optical techniques. We regarded the wz-Mg1-xSn1+xN2 films as magnesium tin oxynitride films (wz-MTNO) because a certain amount of oxygen was unintentionally incorporated into the sputtered wz-Mg1-xSn1+xN2 films. The wz-MTNO layers were n-type degenerate semiconductors with an electron density (n(e)) of the order of 10(20) cm(-3). In films with n(e) > 8 x 10(20) cm(-3), optically extracted resistivities (rho(opt)) obtained via a Drude-fit analysis of the infrared transmittance and reflectance spectra were almost identical to the direct-current resistivities (rho(dc)), indicating that the contribution of grain boundary scattering to the electron transport was negligible. However, the contribution of grain boundary scattering became unignorable with decreasing n(e). The Drude-fit analysis also allowed the determination of the conduction-band effective mass (m(c)*) for the first time. A band edge mass of m(c)*/m(0) & AP; 0.2 (m(0) denotes the free-electron mass) was obtained in the wz-MTNO layers with |x| < 0.1. As x was increased from -0.18 to 0.29, m(c)*/m(0) substantially increased from 0.18 to 0.56, indicating that the conduction-band dispersion decreased. That is, the conduction-band dispersion may be affected by the cation composition x. The findings of this study will provide important information to establish this material as a practical nitride semiconductor.