Preparation and Structure of Low-Melting-point Stannous Chlorophosphate Containing Nitrogen Glasses
Journal of non-crystalline solids(2022)
摘要
P-Sn-O-Cl-N glasses were prepared at 275-450 degrees C, and the optimum melting temperature of the colorless transparent P-Sn-O-Cl-N glasses was 350 degrees C. Series of P-Sn-O-Cl-N glasses were further prepared at 350 degrees C, exhibiting an ultra low glass transition temperature (Tg) of <140 degrees C; the glass forming range were determined. The infrared (IR) and Raman spectra revealed that the Q(1) and Q(2) units of the [PO4] tetrahedral increased and decreased, respectively, with decreasing P/Sn ratio. The unstable P = O bond was destroyed by tin to form a longer P-O-Sn structural chain, which strengthened the crosslinking degree of the glass network structure and increased the Tg and decreased thermal expansion coefficient of the glasses. X-ray photoelectron spectrometry indicated that most Cl ions were bound to cationic Sn2+ and some to NH4+. Moreover, the low-temperature melting reduced the volatilization of Cl- and NH4+ ions, which contributed to the low-melting-point and Tg of the glasses.
更多查看译文
关键词
P-Sn-O-Cl-N glasses,Melting temperature,Glass transition temperature (Tg),Glass structure
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要