Characterization of Nanocrystalline Flake Ribbon for High Frequency Magnetic Cores
IEEE transactions on power electronics(2022)
摘要
This letter reports characterization of the novel nanocrystalline flake ribbon (NFR) soft magnetic material. The comparative analysis among the ferrite N87, N27, and the NFR is presented at different temperature, frequency, and peak magnetic flux density, respectively. Experimental results prove that the NFR has lower loss density, higher magnetic flux density saturation, and better temperature stability from 85 to 300 kHz. A LCL resonant tank based circuit is employed for large signal characterization. The mass-based stacking factor of the NFR core is adopted to describe the core structure. This letter suggests that the NFR is a good alternative to the ferrite for high power magnetic cores due to its superior performance and flexibility structures.
更多查看译文
关键词
Magnetic cores,RLC circuits,Soft magnetic materials,Ferrites,Capacitance,Windings,Stacking,High frequency magnetics,< named-content xmlns:xlink="http:,www,w3,org,1999,xlink" xmlns:ali="http:,www,niso,org,schemas,ali," xmlns:mml="http:,www,w3,org,1998,Math,MathML" xmlns:xsi="http:,www,w3,org,2001,XMLSchema-instance" content-type="math" xlink:type="simple"> < inline-formula > < tex-math notation="LaTeX">$LCL$<,tex-math > <,inline-formula > <,named-content > compensation,nanocrystalline flake ribbon,soft magnetic material characterization
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要