Strengthening Process by Electron Beam to Carbon Fiber for Impact Strength Enhancement of Interlayered Thermoplastic-Polypropylene Carbon Fiber Composite.

Strong adhesion between recyclable thermoplastic (TP) polymer and carbon fiber (CF) has always been highly sought after. Therefore, for an interlayered CF reinforced TP polypropylene (CFRTPP) composite composed of 3 sized CF plies, alternating between 4 PP sheets, designated [PP][CF], a process of activating CF plies directly on both sides with homogeneous low energy electron beam irradiation (EBI) under N gas, prior to lamination assembly and hot press of 4.0 MPa at 493 K for 3 min was carried out. Experimental results showed EBI dose of 43.2, 129, or 216 kGy significantly raised Charpy impact values, at all fracture probabilities, . The 129 kGy dose appeared to be at or near optimum increasing 103%, 83%, and 65% at low-, median-, and high- = 0.07, 0.50, and 0.93; while raising statistically lowest impact value, at = 0 calculated by 3-dimensional Weibull equation about 110%, indicating increased safety and reliability. It is assumed dangling bonds generated by the EBI rapidly form covalent bonds CF:C:O:C:PP and CF:C:C:PP at the interface, along with cross-linking in the PP near the CF. This is by charge transfer from CF to PP.