Reconstruction of vertical alveolar ridge deficiencies utilizing a high-density polytetrafluoroethylene membrane /clinical impact of flap dehiscence on treatment outcomes: case series/

Objectives The aim of this study was to evaluate the effects of membrane exposure during vertical ridge augmentation (VRA) utilizing guided bone regeneration with a dense polytetrafluoroethylene (d-PTFE) membrane and a tent-pole space maintaining approach by registering radiographic volumetric, linear and morphological changes. Methods In 8 cases alveolar ridge defects were accessed utilizing a split-thickness flap design. Following flap elevation VRA was performed with tent-pole space maintaining approach utilizing the combination of a non-reinforced d-PTFE membrane and a composite graft (1:1 ratio of autogenous bone chips and bovine derived xenografts). Three-dimensional radiographic evaluation of hard tissue changes was carried out with the sequence of cone-beam computed tomography (CBCT) image segmentation, spatial registration and 3D subtraction analysis. Results Class I or class II membrane exposure was observed in four cases. Average hard tissue gain was found to be 0.70 cm 3 ± 0.31 cm 3 and 0.82 cm 3 ± 0.40 cm 3 with and without membrane exposure resulting in a 17% difference. Vertical hard tissue gain averaged 4.06 mm ± 0.56 mm and 3.55 mm ± 0.43 mm in case of submerged and open healing, respectively. Difference in this regard was 14% between the two groups. Horizontal ridge width at 9-month follow-up was 5.89 mm ± 0.51 mm and 5.61 mm ± 1.21 mm with and without a membrane exposure respectively, resulting in a 5% difference. Conclusions With the help of the currently reported 3D radiographic evaluation method, it can be concluded that exposure of the new-generation d-PTFE membrane had less negative impact on clinical results compared to literature data reporting on expanded polytetrafluoroethylene membranes.