Macroporous honeycomb-like magnesium oxide fabricated as long-life and outstanding Pb(II) adsorbents combined with mechanism insight

The macroporous honeycomb-like MgO (MHM) had been successfully prepared by hard template method using polystyrene (PS) spheres with different particle sizes of about 400, 600, and 800 nm, respectively. The adsorption performance (3700, 3470, and 3087 mg/g) and specific surface areas (64.0, 51.4, and 34.4 m 2 /g) of MHM materials were inversely proportional to their pore diameters. Among the prepared MHM materials, MHM-400 exhibited the most excellent adsorption performance of 3700 mg/g towards Pb(II) at 25 °C. In this study, the macropore size in MHM played a major role in the adsorption process; Dubinin-Radushkevich (D-R) model further indicated that Pb(II) removal by MHM-400 was dominated by chemical adsorption. The thermodynamic analysis ( ΔG 0 < 0, ΔH 0 > 0, and ΔS 0 > 0) revealed that the Pb(II) adsorption was spontaneous and endothermic. After storing for 360 days, the Pb(II) removal efficiency of MHM-400 was still higher than 98.2%, exhibiting ultra-long life for Pb(II) capture. MHM-400 also exhibited high anti-interference ability towards typically coexisting ions (Na + and K + ). According to the density functional theory (DFT) calculation, the Pb could be adsorbed on the top site of the oxygen atom at the surface of the cubic MgO (200) plane; the adsorption energy ( E ad ) was 0.159 eV. The XRD and FTIR analyses revealed the further formation of Pb 3 (CO 3 ) 2 (OH) 2 and PbO after Pb(II) adsorption. Furthermore, MHM-400 could effectively remove both Cd(II) and Pb(II) ions from wastewater within 20 min, and the adsorption efficiency achieved > 99%, suggesting that MHM-400 was a potential material for effective Pb(II) removal.