Highly Conductive and Ultra Alkaline Stable Anion Exchange Membranes by Superacid-Promoted Polycondensation for Fuel Cells

A series of anion exchange membranes (4-QPPAF-TMA) were prepared by a metal-free, superacid-promoted polymerization reaction. The polymers were obtained with high molecular weight (M-n = 9.5-19.6 kDa, M-w = 44.9-622.5 kDa). 4QPPAF-TMA membranes exhibited high hydroxide ion conductivity (up to 115 mS cm(-1)) at 80 degrees C, reasonable water absorbability (45% water uptake at 30 degrees C for 1.7 meq g(-1)), low to moderate dimensional swelling (5-15% at 30-80 degrees C for 1.7 meq g(-1)), and mechanical robustness (12.8 MPa maximum stress and 32% elongation at break for 1.7 meq g(-1)). Furthermore, 4-QPPAF-TMA membranes exhibited excellent alkaline stability in 8 M KOH at 80 degrees C for 1000 h, maintaining high conductivity (105 mS cm(-1), 97% remaining). density functional theory (DFT) calculations suggested that the unique molecular configuration of the pendant ammonium head groups was responsible for high resistivity to the hydroxide ion attack. A fuel cell was operated with the 4-QPPAFTMA membrane and an ionomer using a non-PGM cathode catalyst (Fe-N-C) to achieve a peak power density of 215 mW cm(-2) accountable for 860 mW mg(-1) Pt at a 590 mA cm(-2) current density and 0.40 V (Pt-C cathode achieved 370 mW cm(-1) at 810 mA cm(-2) and 0.50 V). The fuel cell was operated at constant current density (15 mA cm(-2)) for 240 h with -0.79 mV h(-1) average cell voltage decay. The postdurability analyses revealed that the membrane did not deteriorate while the degradation of the cathode catalysts/ionomer caused the performance loss.