Large-scale bare Cu bonding by 10 gm-sized Cu-Ag composite paste in low temperature low pressure air conditions

Three kinds of Cu-Ag composite paste were fabricated. We used 10 gm Cu particles as the main component of the paste as they are significantly cheaper than Ag and Cu nanoparticles. To understand the bonding performance and mechanism, the flake-shape Cu-Ag pastes with a different solvent and a Cu spherical particle with a diameter of 10 gm were separately implemented for the bare Cu bonding. A detailed and systematic analysis of Cu-Ag paste sintering was performed. In addition, for the flake-shape Cu-Ag paste, the bonding strength and thermal conductivity were evaluated at different sintering temperatures between 180 and 350 & DEG;C. A robust bonding strength of 56.7 MPa was achieved for the SiC chip on bare Cu bonding under low-temperature and low-pressure (300 & DEG;C, 2 MPa) air conditions. In addition, a large area of the direct bonded copper substrate (30 mm x 30 mm) was bonded to the Cu baseplate using Cu-Ag paste. The thermal conductivity of 243.7 W/m & BULL;K was better than that of almost all the Pb-free solders and comparable with the Ag sinter paste. The results revealed that the reducing agent plays a significant role in anti-oxidation and necking growth. This study offers a deeply understand of Cu -Ag composite paste on bare Cu bonding in the air for SiC power devices for its high-temperature applications. & COPY; 2023 Vietnam National University, Hanoi. Published by Elsevier B.V. This is an open access article