Formation of Highly Conductive Interfaces in Crystalline Ionic Liquid-Gated Unipolar MoTe₂/h-BN Field-Effect Transistor

2H MoTe2 (molybdenum ditelluride) has generated significant interest because of its superconducting, nonvolatile memory, and semiconducting of new materials, and it has a large range of electrical properties. The combination of transition metal dichalcogenides (TMDCs) and two dimensional (2D) materials like hexagonal boron nitride (h-BN) in lateral heterostructures offers a unique platform for designing and engineering novel electronic devices. We report the fabrication of highly conductive interfaces in crystalline ionic liquid-gated (ILG) field-effect transistors (FETs) consisting of a few layers of MoTe2/h-BN heterojunctions. In our initial exploration of tellurium-based semiconducting TMDs, we directed our attention to MoTe2 crystals with thicknesses exceeding 12 nm. Our primary focus centered on investigating the transport characteristics and quantitatively assessing the surface interface heterostructure. Our transconductance (g(m)) measurements indicate that the very efficient carrier modulation with an ILG FET is two times larger than standard back gating, and it demonstrates unipolarity of the device. The ILG FET exhibited highly unipolar p-type behavior with a high on/off ratio, and it significantly increased the mobility in MoTe2/h-BN heterochannels, achieving improvement as one of the highest recorded mobility increments. Specifically, we observed hole and electron mobility values ranging from 345 cm(2) V-1 s(-1) to 285 cm(2) V-1 s(-1) at 80 K. We predict that our ability to observe the intrinsic, heterointerface conduction in the channels was due to a drastic reduction of the Schottky barriers, and electrostatic gating is suggested as a method for controlling the phase transitions in the few layers of TMDC FETs. Moreover, the simultaneous structural phase transitions throughout the sample, achieved through electrostatic doping control, presents new opportunities for developing phase change devices using atomically thin membranes.