A Prospective Study of the Assessment of the Efficacy of a Biodegradable Poly(l-lactic acid/ε-caprolactone) Membrane for Guided Bone Regeneration

Biodegradable guided bone regeneration (GBR) membranes consist primarily of collagen and aliphatic polyesters. This study assessed the comparative efficacy of a poly(l-lactic-caprolactone) [P(LA/CL)] membrane versus that of a collagen membrane in GBR. Patients requiring GBR simultaneously or before dental implant placement in edentulous regions were randomly assigned to one of two membranes. Within each membrane, they were subdivided into 3 groups: dental implants were placed simultaneously with GBR in groups A and B, and 180 days post-GBR in group C. The augmented bone width was measured at 1, 3, and 6 mm from the implant’s neck (groups A and B) or the reference line (group C), utilizing cone-beam computed tomography images, immediately and 150 days post-surgery. A histological study was performed to evaluate bone formation in group C. No adverse events were observed. In the collagen group, the absorbed ratios of the augmented bone were 40.9 ± 36.7%, 29.4 ± 30.1%, and 11.1 ± 22.0% at 1, 3, and 6 mm, respectively; the ratio at 6 mm was significantly lower than that at 1 mm (p = 0.0442). In the P(LA/CL) group, those were 26.2 ± 27.3%, 17.1 ± 19.7%, and 13.3 ± 16.4% at 1, 3, and 6 mm, respectively, with no significant difference at each point. No significant inter-membrane differences were observed. The bone augmentation potential of the P(LA/CL) membrane matched that of the collagen membrane. P(LA/CL) could be used as a safe and effective membrane in GBR.