Electrical, thermal and noise properties of platinum-carbon free-standing nanowires designed as nanoscale resistive thermal devices

Platinum-carbon (PtC) composite nanowires were fabricated using focused electron beam induced deposition and postprocessed, and their performance as a nanoscale resistive thermal device (RTD) was evaluated. Nanowires were free-standing and deposited on a dedicated substrate to eliminate the influence of the substrate itself and of the halo effect on the results. The PtC free-standing nanowires were postprocessed to lower their electrical resistance using electron beam irradiation and thermal annealing using Joule heat both separately and combined. Postprocessed PtC free-standing nanowires were characterized to evaluate their noise figure (NF) and thermal coefficients at the temperature range from 30 K to 80 degrees C. The thermal sensitivity of RTD was lowered with the reduced resistance but simultaneously the NF improved, especially with electron-beam irradiation. The temperature measurement resolution achievable with the PtC free-standing nanowires was 0.1 K in 1 kHz bandwidth.