Recycling Cobalt from Spent Lithium-Ion Batteries for Designing the Novel Cobalt Nitride Followers: Towards Efficient Overall Water Splitting and Advanced Zinc-Air Batteries.

Although cobalt nitride (CoN)-based nanomaterials have been widely designed as advanced oxygen evolution reaction (OER), hydrogen evolution reaction (HER), and oxygen reduction reaction (ORR) catalysts, the continuous consumption of lithium-ion batteries (LIBs) has led to a high price of cobalt metal. Therefore, in the future, recycling valuable Co elements from spent devices and boosting their service efficiency will inevitably promote the utilization of Co-based materials in water splitting and zinc-air batteries (ZABs). Herein, we realize the Co recycling from spent LIBs by a simple hydrometallurgy method. Under the assistance of hexamethylenetetramine and polystyrene spheres, after the hydrothermal and pyrolysis treatment in the NH3 atmosphere, the as-reclaimed cobalt oxalates were successfully transformed into novel three-dimensional (3D) CoN nanoflowers (denoted as CoN NFs). Benefiting from the unique 3D flower-like architectures, intrinsic high conductivity, large surface area, uniformly dispersed CoN nanoparticles, and the synergistic effect between Co3N and CoO phases, the 3D flower-like CoN NFs exhibited excellent OER catalytic activity. The performance was much better than commercial RuO2 in the 1.0 M KOH solution. Furthermore, the CoN NFs-based water splitting cell needed a voltage of 1.608 V to achieve the current density of 10 mA cm -2, which is even 16 mV smaller than that of Pt/CIIRuO2 benchmark (1.624 V). Meanwhile, the CoN NFs-derived ZAB exhibited a high peak power density of 107.3 mW cm -2 (vs. 103.2 mW cm -2 of Pt/C-RuO2-based ZAB) and a low charge-discharge voltage gap (0.93 V vs. 1.43 V of Pt/C-RuO2-based ZAB). Due to the excellent structural and elemental stabilities, the corresponding water splitting cell and ZAB had outstanding durability. This work successfully explored an advanced industrial chain from recycling Co metal in spent devices to designing the high -efficiency HER/OER/ORR electrocatalysts for advanced water splitting devices and ZABs. This will further promote the value-added utilization of valuable Co metal in various energy storage or conversion devices.