A Comparative Study on the Passive Film and SCC Behavior of Ti-6Al-3Nb-2Zr-1Mo Alloy at Various Test Temperatures in Simulated Seawater

In this work, the electrochemical and stress corrosion cracking (SCC) behavior of Ti-6Al-3Nb-2Zr-1Mo alloy in simulated seawater at various solution temperatures were systematically studied. Results show rising test temperature increases the point defect density in passive film and deteriorates the stability. Therefore, SCC is promoted by localized anodic dissolution (AD). At 25 degrees C, SCC initiates in alpha p phase, and (3 phase hinders SCC propagation on account of the lower electrochemical activity induced by element segregation. While at 4 degrees C, the SCC propagation rate is higher than that at 25 degrees C, as the SCC propagation resistance of (3 phases decreases.