通过氧化沉淀、还原溶解等工艺从钛阳极退镀料溶解液中回收贵金属铱,实验确定了最佳工艺条件,在氧化还原电位大于 900 mV、氯化铵用量为铱的 1 倍以上时,铱的沉淀率大于 98%,还原pH值为 3 时,可较好的分离铱中少量的铂钯铑钌杂质.方法适用于以铱为主体、贵金属杂质含量较低的含铱废料处理,操作简便,产品纯度可达到国标要求.
As the energy conversion unit of proton exchange membrane fuel cell (PEMFC), membrane electrode assembly (MEA) converted chemical energy into electrical energy under the action of catalyst. Platinum-based catalyst was still an irreplaceable catalyst for commercial PEMFC, and the platinum (Pt) loading in membrane electrode had became an important indicator of PEMFC performance evaluation. By improving the existing national standard method for testing the platinum loading of PEMFC membrane electrode, a microwave digestion pretreatment method for testing the platinum loading of PEMFC membrane electrode was developed. Compared with the national standard method, the new method not only improved the accuracy of the test results, but also greatly improved the test efficiency. The amount of reagent was greatly reduced. The method was more green, safe and environmentally friendly.
以 1-苯基异喹啉(piq)为主配体,以 3-甲基-2-吡啶甲酸(mecid)为辅助配体合成了一种铱(Ⅲ)配合物 Ir(piq)2(mecid).采用元素分析、红外光谱、核磁共振谱分析和单晶 X 射线衍射对其化学组成和结构进行了表征.采用热失重(TGA)曲线分析了其热稳定性质,热分解温度为 325℃.采用紫外-可见光谱和光致发光光谱对其光物理性质进行了分析.结果表明,化学组成为C37H26IrN3O2,属于三斜晶系,P1/n 空间群.晶胞参数为 a=8.3130(4)nm,b=11.4866(5)nm,c=15.3737(7)nm,α=75.726(2)°,β=83.005(2)°,γ=88.785(2)°,V=1.4120(11)nm3,Z=2.光物理性质显示最大发射波长为 618 nm,为红色发射的铱磷光配合物.
为了提高PtIr高温合金电火花线切割加工的表面质量及减少切割边缘毛刺,研究电流、脉宽、脉间距对PtIr合金电火花线切割加工效果的影响.结果表明:加工过程的参数对材料的表面粗糙度及边缘毛刺有重要影响.对电火花线切割加工工艺参数进行了优化,电流为 5 A、脉宽 5 μs、脉距 5 μs时、加工速度150 步/S、钼丝直径0.1 mm时加工效果最佳,表面粗糙度Ra值为0.14 μm,切割精度公差可控制在±0.006 mm内.
甲烷是第二大温室气体,其年度增温潜能是CO2的 26～28 倍.天然气车排放尾气中的主要成分为未燃烧完全的甲烷和高浓度的水(高达 20%),目前已有大量研究表明水会严重影响Pd活性组分的催化活性及氧化铝载体的催化稳定性,因此如何在高含水废气中处理这些甲烷一直是天然气车后处理催化剂的研究热点.本研究采用等体积浸渍法制备了改性载体(AlLa5、AlLa10 和AlLa15),并用过量浸渍法将 0.5%Pd负载到改性载体Al2O3-La和未改性载体γ-Al2O3 上,同时考察了La的引入比例对催化剂催化甲烷氧化中的耐水热性能影响,用N2物理吸脱附、CO脉冲吸附、XPS和XRD等方法对所制备催化剂进行表征.结果表明,La的加入明显提高催化剂在催化甲烷氧化中的耐水热性能,其中Pd/AlLa5 表现出最优异的耐水热稳定性.