Structural, Optical and Vibrational Properties of ZnO:M (m=al3+ and Sr2+) Nano and Micropowders Grown by Hydrothermal Synthesis

Powders of ZnO and ZnO:M (M = Al3+ and Sr2+) with 1 and 4% of M nominal content were synthetized by a hydrothermal method in a diethanolamine (DEA) medium. The samples were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDX), micro-Raman and photoluminescence (PL). The powder particles were spherical with average radius decreasing from 1 mu m down to 70 nm with increasing Al3+ nominal content but nearly independent on the Sr2+ nominal content. The XRD and micro-Raman results indicate that both Al3+ and Sr2+ mostly incorporated substitutionally into the ZnO lattice, giving rise to compressive and tensile strain, respectively, as a result of ionic radii differences. The PL spectra for ZnO:Al exhibit a dopant-induced contribution at similar to 3.1 eV, which is not observed for ZnO:Sr, due to radiative transitions involving trapping of photocarriers at theoretically expected substitutional Al3+ donor states or at Zn interstitial defects. (C) 2019 Elsevier B.V. All rights reserved.