Supported platinum nanoparticle catalysts are known to convert polyolefins to high-quality liquid hydrocarbons using hydrogen under relatively mild conditions. To date, few studies using platinum grafted onto various metal oxide (M x O y ) supports have been undertaken to understand the role of the acidity of the oxide support in the carbon-carbon bond cleavage of polyethylene under consistent catalytic conditions. Specifically, two Pt/MxOy catalysts (MxOy = SrTiO3 and SiO2-Al(2)O3; Al = 3.0 wt %, target Pt loading 2 wt % Pt similar to 1.5 nm), under identical catalytic polyethylene hydrogenolysis conditions (T = 300 degree celsius, P(H2) = 170 psi, t = 24 h; M-w = similar to 3,800 g/mol, M-n = similar to 1,100 g/mol, D = 3.45, N-branch/100C = 1.0), yielded a narrow distribution of hydrocarbons with molecular weights in the range of lubricants (M-w = < 600 g/mol; M-n < 400 g/mol; D = 1.5). While Pt/SrTiO3 formed saturated hydrocarbons with negligible branching, Pt/SiO2-Al2O3 formed partially unsaturated hydrocarbons (<1 mol % alkenes and similar to 4 mol % alkyl aromatics) with increased branch density (N-branch/100C = 5.5). Further investigations suggest evidence for a competitive hydrocracking mechanism occurring alongside hydrogenolysis, stemming from the increased acidity of Pt/SiO2-Al2O3 compared to Pt/SrTiO3. Additionally, the products of these polymer deconstruction reactions were found to be independent of the polyethylene feedstock, allowing the potential to upcycle polyethylenes with various properties into a value-added product.
原文链接
分享
引用