Preparation and characterisation of poly p-phenylene-2,6-benzobisoxazole fibre-reinforced resin matrix composite for endodontic post material: A preliminary study

Objectives Currently used fibre-reinforced composite (FRC) intracanal posts possess low flexural strength which usually causes post fracture when restoring teeth with extensive loss. To improve the flexural strength of FRC, we aimed to apply a high-performance fibre, poly p-phenylene-2, 6-benzobisoxazole (PBO), to FRCs to develop a new intracanal post material. Methods To improve the interfacial adhesion strength, the PBO fibre was treated with coupling agent (Z-6040), argon plasma, or a combination of above two methods. The effects of the surface modifications on PBO fibre were characterised by determining the single fibre tensile strength and interfacial shear strength (IFSS). The mechanical properties of PBO FRCs were characterised by flexural strength and flexural modulus. The cytotoxicity of PBO FRC was evaluated by the MTT assay. Results Fibres treated with a combination of Z-6040 and argon plasma possessed a significantly higher IFSS than untreated fibres. Fibre treated with the combination of Z-6040-argon-plasma FRC had the best flexural strength (531.51±26.43MPa) among all treated fibre FRCs and had sufficient flexural strength and appropriate flexural moduli to be used as intracanal post material. Furthermore, an in vitro cytotoxicity assay confirmed that PBO FRCs possessed an acceptable level of cytotoxicity. Conclusions In summary, our study verified the feasibility of using PBO FRC composites as new intracanal post material. Although the mechanical property of PBO FRC still has room for improvement, our study provides a new avenue for intracanal post material development in the future. Clinical significance To our knowledge, this is the first study to verify the feasibility of using PBO FRC composites as new intracanal post material. Our study provided a new option for intracanal post material development.