Fabrication of micron size Nb/Al-Al2O3/Nb junctions with a trilevel resist liftoff process

Magnetics, IEEE Transactions  (1991)

引用 26|浏览4
暂无评分
摘要
A trilevel resist, consisting of polyimide planarization, SiO2 barrier, and photoresist, was used to pattern junction areas in Nb/Al-Al2O3/Nb trilayer films. After reactive ion etching to define the junction areas, the perimeter of the junction was revealed, and excellent liftoff structures were defined with an oxygen plasma shrink of the exposed polyimide sidewalls. A subsequently deposited insulation layer seals the sides and the top surface along the perimeter of the Nb counter electrode button. High-quality superconductor-insulator-superconductor (SIS) junctions with diameters as small as 1.2 μm and Vm as large as 1500 mV at 2.0 K have been fabricated. An SIS receiver using these junctions with integrated tuning elements has a DSB noise temperature of 58 K at 230 GHz. This is believed to be the lowest receiver noise temperature ever reported at this frequency
更多
查看译文
关键词
alumina,aluminium,electron device noise,mixers (circuits),niobium,solid-state microwave devices,superconducting junction devices,1.2 micron,1.5 v,2 k,230 ghz,dsb noise temperature,nb counter electrode,nb-al-al2o3-nb,sis junctions,sis receiver,sio2 barrier,diameters,integrated tuning elements,liftoff structures,photoresist,polyimide planarization,reactive ion etching,receiver noise temperature,superconductor-insulator-superconductor,trilevel resist liftoff process,superconductors
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要