Electrochemical Properties Of Sr1-Xcexmno3 (0.1 <= X <= 0.4) - Gdc Composite Cathodes For It-Sofcs

The electrochemical properties of Sr1-xCexMn0.3 (0.1 <= x <= 0.4) Gd0.2Ce0.8O2-x (GDC) composite cathodes were determined by impedance spectroscopy. The study focused on the doping effect of Ce in the composite cathodes. Single-phase perovskite was obtained for 0.1 x < 0.3 in SCM. No reaction occurred between the Sr0.7Ce0.3Mn0.3 electrode and the GDC electrolyte at an operating temperature of 800 degrees C for 100 h. In the single phase perovskite region, lattice expansion occurred due to the reduction of Mn4+ to Mn3+ at B-sites, and this was attributed to an increase in Ce content. Ce doping enhanced the electrode performance of SCM GDC composite cathodes, and best electrode performance was achieved for the Sr0.7Ce0.3Mn0.3 GDC composite cathode (0.93 52 cm2 and 0.47 CI cm2 at 750 C and 800 C, respectively). The improvement in electrode performance was attributed to increases in charge carriers induced by a shift of some Mn from +4 to +3 and to the formation of surface oxygen vacancies caused by Mn4+ to Mn3+ conversion at high temperatures. (C) 2013 Elsevier Ltd and Techna Group S.r.l. All rights reserved.